● Product Introduction:
The content of zirconia in the beads is approximately 65% and so it is usually called "65 Zirconium". With the advanced process of roll polishing and high temperature sintering, there will be no pore and void inside the beads. Because of medium density and hardness, it will be suitable for the grinding of materials with medium and low viscosity and it can be used in most of the grinding equipment. The small size beads are usually used as high0end ball blast for polishing and removal of flaws.
● Product Specification:
Composition | ZrO2 65% SiO2 35% | Size (mm) |
Real Density | 4.0g/cm3 |
0.6-0.8 0.8-1.0 1.0-1.2 1.2-1.4 1.4-1.6 1.6-1.8 1.0-2.0 2.0-2.5 2.5-3.0 ............
|
Bulk Density | 2.5g/cm3 | |
Moh's Hardness | 8 | |
Wear Rate Per Ton | 0.03kg/h | |
Color | White | |
Package | 25kg/barrel |
● Features:
a. High strength and hardness
b. High density
c. Good spherical degree
d. High Wear-resisting property.
e. Smooth surface,easy clean,Reduce the internal friction between beads and improve the material flow efficiency.
● Applications:
Grinding,Dispersing,etc.
For Paint;Printing ink;Paint coating;Ceramic color;Pigment,etc.
● Production & Packing:
● Package & Delivery:
20~25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped
● Storage:
The grinding media should be stored in a dry and clean place.
● Product Introduction:
The content of zirconia in the beads is approximately 65% and so it is usually called "65 Zirconium". With the advanced process of roll polishing and high temperature sintering, there will be no pore and void inside the beads. Because of medium density and hardness, it will be suitable for the grinding of materials with medium and low viscosity and it can be used in most of the grinding equipment. The small size beads are usually used as high0end ball blast for polishing and removal of flaws.
● Product Specification:
Composition | ZrO2 65% SiO2 35% | Size (mm) |
Real Density | 4.0g/cm3 |
0.6-0.8 0.8-1.0 1.0-1.2 1.2-1.4 1.4-1.6 1.6-1.8 1.0-2.0 2.0-2.5 2.5-3.0 ............
|
Bulk Density | 2.5g/cm3 | |
Moh's Hardness | 8 | |
Wear Rate Per Ton | 0.03kg/h | |
Color | White | |
Package | 25kg/barrel |
● Features:
a. High strength and hardness
b. High density
c. Good spherical degree
d. High Wear-resisting property.
e. Smooth surface,easy clean,Reduce the internal friction between beads and improve the material flow efficiency.
● Applications:
Grinding,Dispersing,etc.
For Paint;Printing ink;Paint coating;Ceramic color;Pigment,etc.
● Production & Packing:
● Package & Delivery:
20~25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped
● Storage:
The grinding media should be stored in a dry and clean place.
●Chemical Composition:
Composition | ZrO₂ | SiO₂ |
Content % | 65 | 35 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Moh’s | Hardness Hv | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | light yellow |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 | 4 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 | 5 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 | 6 |
●Chemical Composition:
Composition | ZrO₂ | SiO₂ |
Content % | 65 | 35 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Moh’s | Hardness Hv | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | light yellow |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 | 4 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 | 5 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 | 6 |