Availability: | |
---|---|
Quantity: | |
1. Main Advantage of the zirconia bead/ball
Excellent wear resistance, Weight loss of ball lee of 4ppm,
High density, grinding efficiency,
No impurity, keep the material high degree of purity.
2. Main Use of the zirconia bead/ball
Electronic material (Such as BaTiO3,BaCO3), Magnetic bands superfine grinding,
Paint,pigment, Coatings dispesing and superfine grinding,
Ceramic glaze(zirconia sand) superfine grinding,
Medication, Cosmetic dispersing and superfine grinding.
Composition | ZrO2:94.8±0.2%, Y2O3: 5.1±0.1% |
Density | ≥6.02g/cm3 |
Bulk density | ≥3.70g/cm3 |
Hardness | 9 Mohs |
Crushing Load | >2.0 KN(2mm) |
Water Absorption | 0% |
Material | Zirconia Ceramic |
Compressive Strength | 5500MPa |
Flexural Strength | 8 MPa.m1/2 |
Modulus of Elasticity | 200Gpa |
Thermal Conductivity | 3W/(m.K) (20-400℃) |
Thermal Expansivity | 9.6* 10 -6 K -1 |
Fracture Toughness | 8MPa.m0.5 |
Grain Size | ≤0.5um |
Size | 0.08-50mm |
1. the efficiency of grinding is high: yttrium stabilized TZP zirconia ceramic microbeads are 1.6 times as high as that of ordinary zirconia beads, with higher grinding efficiency under the same conditions.
2.good fluidity: the product has good roundness, smooth surface, and lower wear and tear on equipment than other grinding medials.
3.impact resistance and low wear: TZP zirconia ceramic beads have good toughness, and do not crack, open and peel in high speed and high concentration machines, and wear only 2 / 1 of zirconium silicate beads.
4. the use cost is low: choosing this product will bring you the reduction of comprehensive cost such as dielectric wear, electricity consumption, labor and equipment and so on, and the quality of products will be greatly improved.
● Applications
● Factory Equipment
● Packing & Delivery:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
● Storage:
The grinding media should be stored in a dry and clean place.
●FAQ
A: Please send your drawing or the details of your demand to us, then we will quote to you.
A: Generally it will take about 25-30 days because the production process is a long time cycle, but if we have stock of the products you need, then we can ship out once we get the payment.
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
A: We required 100% TT payment in advance because the products are customized.
1. Main Advantage of the zirconia bead/ball
Excellent wear resistance, Weight loss of ball lee of 4ppm,
High density, grinding efficiency,
No impurity, keep the material high degree of purity.
2. Main Use of the zirconia bead/ball
Electronic material (Such as BaTiO3,BaCO3), Magnetic bands superfine grinding,
Paint,pigment, Coatings dispesing and superfine grinding,
Ceramic glaze(zirconia sand) superfine grinding,
Medication, Cosmetic dispersing and superfine grinding.
Composition | ZrO2:94.8±0.2%, Y2O3: 5.1±0.1% |
Density | ≥6.02g/cm3 |
Bulk density | ≥3.70g/cm3 |
Hardness | 9 Mohs |
Crushing Load | >2.0 KN(2mm) |
Water Absorption | 0% |
Material | Zirconia Ceramic |
Compressive Strength | 5500MPa |
Flexural Strength | 8 MPa.m1/2 |
Modulus of Elasticity | 200Gpa |
Thermal Conductivity | 3W/(m.K) (20-400℃) |
Thermal Expansivity | 9.6* 10 -6 K -1 |
Fracture Toughness | 8MPa.m0.5 |
Grain Size | ≤0.5um |
Size | 0.08-50mm |
1. the efficiency of grinding is high: yttrium stabilized TZP zirconia ceramic microbeads are 1.6 times as high as that of ordinary zirconia beads, with higher grinding efficiency under the same conditions.
2.good fluidity: the product has good roundness, smooth surface, and lower wear and tear on equipment than other grinding medials.
3.impact resistance and low wear: TZP zirconia ceramic beads have good toughness, and do not crack, open and peel in high speed and high concentration machines, and wear only 2 / 1 of zirconium silicate beads.
4. the use cost is low: choosing this product will bring you the reduction of comprehensive cost such as dielectric wear, electricity consumption, labor and equipment and so on, and the quality of products will be greatly improved.
● Applications
● Factory Equipment
● Packing & Delivery:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
● Storage:
The grinding media should be stored in a dry and clean place.
●FAQ
A: Please send your drawing or the details of your demand to us, then we will quote to you.
A: Generally it will take about 25-30 days because the production process is a long time cycle, but if we have stock of the products you need, then we can ship out once we get the payment.
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
A: We required 100% TT payment in advance because the products are customized.
●Chemical Composition:
Composition | ZrO₂ | Y₂O₃ | Other |
Content % | 94.8±0.2 | 5.1±0.1 | 0.1% |
●Physical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load KN(Φ2.0mm) | Grain size | Wear loss | Sphericity |
≥6.02 | ≥ 3.70 | ≥1250 | 9 | ≥20 | ≤0.5 | ≤0.08 | ≥98 |
● Ball Sizes :
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ0.08-0.12 | Φ0.12-0.18 | Φ0.18-0.22 | Φ0.22-0.28 | Φ0.28-0.35 |
Φ0.3-0.4 | Φ0.4-0.6 | Φ0.6-0.8 | Φ0.8-1.0 | Φ1.0-1.2 |
Φ1.2-1.4 | Φ1.4-1.6 | Φ1.6-1.8 | Φ1.8-2.0 | 2.0-2.2 |
Φ2.2-2.4 | Φ2.4-2.6 | Φ2.6-2.8 | Φ2.8-3.0 | Φ3.0-3.2 |
Φ3.2-3.5 | Φ4 | Φ5 | Φ6 | Φ7 |
Φ8 | Φ10 | Φ12 | Φ15 | Φ17 |
Φ20 | Φ25 | Φ30 | Φ40 | Φ50 |
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ3*3 | Φ5*5 | Φ7*7 | Φ10*10 | Φ12.7*12.7 | Φ15*15 |
●Chemical Composition:
Composition | ZrO₂ | Y₂O₃ | Other |
Content % | 94.8±0.2 | 5.1±0.1 | 0.1% |
●Physical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load KN(Φ2.0mm) | Grain size | Wear loss | Sphericity |
≥6.02 | ≥ 3.70 | ≥1250 | 9 | ≥20 | ≤0.5 | ≤0.08 | ≥98 |
● Ball Sizes :
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ0.08-0.12 | Φ0.12-0.18 | Φ0.18-0.22 | Φ0.22-0.28 | Φ0.28-0.35 |
Φ0.3-0.4 | Φ0.4-0.6 | Φ0.6-0.8 | Φ0.8-1.0 | Φ1.0-1.2 |
Φ1.2-1.4 | Φ1.4-1.6 | Φ1.6-1.8 | Φ1.8-2.0 | 2.0-2.2 |
Φ2.2-2.4 | Φ2.4-2.6 | Φ2.6-2.8 | Φ2.8-3.0 | Φ3.0-3.2 |
Φ3.2-3.5 | Φ4 | Φ5 | Φ6 | Φ7 |
Φ8 | Φ10 | Φ12 | Φ15 | Φ17 |
Φ20 | Φ25 | Φ30 | Φ40 | Φ50 |
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ3*3 | Φ5*5 | Φ7*7 | Φ10*10 | Φ12.7*12.7 | Φ15*15 |