● Features:
Good roundness and smooth surface;
Unique formula, patented;
Superior performance-price ratio to other low-medium density media like glass and alumina beads;
Substitutes glass beads by increasing milling efficiency and reducing mill wear.
● Applications:
Coating, paints, inks, pigments and dyes.
Mineral fillers e.g. TiO2 , GCC , Zircon and Kaolin
Gold, silver, platinum, lead, copper and zinc sulfide.
● Package:
20~25KG/bag, 800-1000KG/Pallet with shrink wrapped.
● Storage:
The grinding media should be stored in a dry and clean place.
● Features:
Good roundness and smooth surface;
Unique formula, patented;
Superior performance-price ratio to other low-medium density media like glass and alumina beads;
Substitutes glass beads by increasing milling efficiency and reducing mill wear.
● Applications:
Coating, paints, inks, pigments and dyes.
Mineral fillers e.g. TiO2 , GCC , Zircon and Kaolin
Gold, silver, platinum, lead, copper and zinc sulfide.
● Package:
20~25KG/bag, 800-1000KG/Pallet with shrink wrapped.
● Storage:
The grinding media should be stored in a dry and clean place.
●Chemical Composition:
Composition | ZrO₂ | SiO₂ | Al₂O₃ | Others |
Content % | 20 | 40 | 35 | 5 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness HV | Color |
≥3.2 | >1.7 | >760 | white |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.8 | 1.4 – 1.7 | 2.5 – 3.0 | 4.5 – 5.5 |
0.8-1.2 | 1.5 – 2.0 | 3.0-4.0 | 5.0-6.0 |
1.2 – 1.4 | 2.0 – 2.5 | 4.0-4.5 | 6.0-7.0 |
●Chemical Composition:
Composition | ZrO₂ | SiO₂ | Al₂O₃ | Others |
Content % | 20 | 40 | 35 | 5 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness HV | Color |
≥3.2 | >1.7 | >760 | white |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.8 | 1.4 – 1.7 | 2.5 – 3.0 | 4.5 – 5.5 |
0.8-1.2 | 1.5 – 2.0 | 3.0-4.0 | 5.0-6.0 |
1.2 – 1.4 | 2.0 – 2.5 | 4.0-4.5 | 6.0-7.0 |