●Product Introdution:
Cerium stabilized zirconia grinding the proportion of referrals is the grinding of zirconia referred the largest (based on customer needs the production of products 6.0 g/cm3), from the dynamics in terms of (EC = 1/2mv2) if the use of cerium polishing equipment stabilized zirconia grinding can be referred to a larger impact energy, thereby enhancing production efficiency; especially for high viscosity or abrasive products with high solid and easier to show its advantages. The low viscosity of the product, as a result of the option at a fixed volume of the smaller Ce-stabilized zirconia abrasive grinding surface area increased referrals, and then grinding to obtain better results.
●Feature:
Micro-structure of delicate, uniform, dense ceramics of the Quartet, it has a gem-like hardness and density, is a series of grinding all the zirconium-mediated a most Shen. Its excellent wear resistance and fracture toughness is particularly suited for high-solid-phase high-viscosity, high hardness of the paste for grinding and dispersion of pure; good match at the same time high input energy and the high shear machine sanding.
●Physical Parameterts:
Chemical Composition | 83-87% ZrO2 9-13% CeO2 <2.0% Others |
Bulk Density | ≥3.75g/cm3 |
Density | >6.0g/cm3 |
Compressive strength | >1.5KN (Φ2mm) |
Vickers hardness | >1150 |
Self consumption (ppm/h) | <0.8 |
Roundness | ≥0.97(Xmin/Xmax) |
●Size Available:
0.3-0.4 | 0.4-0.6 | 0.6-0.8 | 0.8-1.0 | 1.0-1.2 |
1.2-1.4 | 1.4-1.6 | 1.6-1.8 | 1.8-2.0 | 2.0-2.2 |
2.2-2.4 | 2.4-2.6 | 2.6-2.8 | 2.8-3.0 | 3.0-3.2 |
4 | 5 | 10 | 15 | 20 |
Remarks:We could also produce customized products as to customer’s request.
●Feature:
It has a gem-like hardness and density.Micro-structure of delicate, uniform, dense ceramics of the Quartet. Its excellent wear resistance and fracture toughness is particularly suited for grinding and dispersing high-solid-phase high-viscosity, high hardness of the paste.
(1).Long working life: 30 times longer life than glass beads, 6 times than zirconium silicate beads.
(2)High grindingefficiency: around 6 times than glass beads; 2 times than zirconium silicate bead
(3).Excellent wear resistance and fracture toughness.
●Laboratory Equipment:
●Packing & Delivery:
●Package:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
●Storage:
The grinding media should be stored in a dry and clean place.
●Product Introdution:
Cerium stabilized zirconia grinding the proportion of referrals is the grinding of zirconia referred the largest (based on customer needs the production of products 6.0 g/cm3), from the dynamics in terms of (EC = 1/2mv2) if the use of cerium polishing equipment stabilized zirconia grinding can be referred to a larger impact energy, thereby enhancing production efficiency; especially for high viscosity or abrasive products with high solid and easier to show its advantages. The low viscosity of the product, as a result of the option at a fixed volume of the smaller Ce-stabilized zirconia abrasive grinding surface area increased referrals, and then grinding to obtain better results.
●Feature:
Micro-structure of delicate, uniform, dense ceramics of the Quartet, it has a gem-like hardness and density, is a series of grinding all the zirconium-mediated a most Shen. Its excellent wear resistance and fracture toughness is particularly suited for high-solid-phase high-viscosity, high hardness of the paste for grinding and dispersion of pure; good match at the same time high input energy and the high shear machine sanding.
●Physical Parameterts:
Chemical Composition | 83-87% ZrO2 9-13% CeO2 <2.0% Others |
Bulk Density | ≥3.75g/cm3 |
Density | >6.0g/cm3 |
Compressive strength | >1.5KN (Φ2mm) |
Vickers hardness | >1150 |
Self consumption (ppm/h) | <0.8 |
Roundness | ≥0.97(Xmin/Xmax) |
●Size Available:
0.3-0.4 | 0.4-0.6 | 0.6-0.8 | 0.8-1.0 | 1.0-1.2 |
1.2-1.4 | 1.4-1.6 | 1.6-1.8 | 1.8-2.0 | 2.0-2.2 |
2.2-2.4 | 2.4-2.6 | 2.6-2.8 | 2.8-3.0 | 3.0-3.2 |
4 | 5 | 10 | 15 | 20 |
Remarks:We could also produce customized products as to customer’s request.
●Feature:
It has a gem-like hardness and density.Micro-structure of delicate, uniform, dense ceramics of the Quartet. Its excellent wear resistance and fracture toughness is particularly suited for grinding and dispersing high-solid-phase high-viscosity, high hardness of the paste.
(1).Long working life: 30 times longer life than glass beads, 6 times than zirconium silicate beads.
(2)High grindingefficiency: around 6 times than glass beads; 2 times than zirconium silicate bead
(3).Excellent wear resistance and fracture toughness.
●Laboratory Equipment:
●Packing & Delivery:
●Package:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
●Storage:
The grinding media should be stored in a dry and clean place.
●Chemical Composition:
Composition | ZrO₂ | CeO₂ + Others |
Content % | ≥80 | ≤20 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Bending Strength MPa | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load Kgf(Φ1.50mm) | Sphericity (%) |
≥5.95 | ≥3.70 | 1000-1200 | ≥1150 | 7 | ≥70 | ≥98 |
●Sizes Φ:
Size (mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.6-2.8 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 2.8-3.0 |
Note: Size can be customized as per request.
●Chemical Composition:
Composition | ZrO₂ | CeO₂ + Others |
Content % | ≥80 | ≤20 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Bending Strength MPa | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load Kgf(Φ1.50mm) | Sphericity (%) |
≥5.95 | ≥3.70 | 1000-1200 | ≥1150 | 7 | ≥70 | ≥98 |
●Sizes Φ:
Size (mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.6-2.8 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 2.8-3.0 |
Note: Size can be customized as per request.