● Product Introduction:
Duratec zirconium silicate grinding beads are made of first-class zircon sand by rolling and sintering. Unique formula and production process provide a true meaning of zirconium silicate beads with medium density and hardness, Duratec zirconium silicate grinding beads with the character of high compressive strength and low wear.
● Product Specification:
Chemical Composition:
Composition | ZrO2 | SiO2 |
Content % | 65% | 35% |
Typical Properties:
Specific Gravity g/cm3 | Bulk Density kg/L | Hardness Moh's | Hardness HV1 | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | Ivory white |
Sizes Φ:
Size (mm) | Size (mm) | Size (mm) | Size (mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 |
● Features:
a. High strength and hardness
b. High density
c. Good spherical degree
d. High Wear-resisting property.
e. Smooth surface,easy clean,Reduce the internal friction between beads and improve the material flow efficiency.
● Applications:
(1) Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and other minerals;
(2) Dielectric materials, piezoelectric materials, capacitor;
(3) Ceramic glazes and frits;
(4) Coatings, paints, inks etc;
(5) Metallic minerals like copper, silver, nickel, gold, zinc etc;
(6) Recommend to be used in stirred mill and ball mill.
● Production & Packing:
● Package & Delivery:
20~25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped
● Storage:
The grinding media should be stored in a dry and clean place.
● Product Introduction:
Duratec zirconium silicate grinding beads are made of first-class zircon sand by rolling and sintering. Unique formula and production process provide a true meaning of zirconium silicate beads with medium density and hardness, Duratec zirconium silicate grinding beads with the character of high compressive strength and low wear.
● Product Specification:
Chemical Composition:
Composition | ZrO2 | SiO2 |
Content % | 65% | 35% |
Typical Properties:
Specific Gravity g/cm3 | Bulk Density kg/L | Hardness Moh's | Hardness HV1 | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | Ivory white |
Sizes Φ:
Size (mm) | Size (mm) | Size (mm) | Size (mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 |
● Features:
a. High strength and hardness
b. High density
c. Good spherical degree
d. High Wear-resisting property.
e. Smooth surface,easy clean,Reduce the internal friction between beads and improve the material flow efficiency.
● Applications:
(1) Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and other minerals;
(2) Dielectric materials, piezoelectric materials, capacitor;
(3) Ceramic glazes and frits;
(4) Coatings, paints, inks etc;
(5) Metallic minerals like copper, silver, nickel, gold, zinc etc;
(6) Recommend to be used in stirred mill and ball mill.
● Production & Packing:
● Package & Delivery:
20~25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped
● Storage:
The grinding media should be stored in a dry and clean place.
●Chemical Composition:
Composition | ZrO₂ | SiO₂ |
Content % | 65 | 35 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Moh’s | Hardness Hv | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | light yellow |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 | 4 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 | 5 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 | 6 |
●Chemical Composition:
Composition | ZrO₂ | SiO₂ |
Content % | 65 | 35 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Moh’s | Hardness Hv | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | light yellow |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 | 4 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 | 5 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 | 6 |