●Product Introdution:
It is with the earth rare element “cerium”, so cerium stabilized zirconia bead has the biggest specific gravity in all zirconia beads series and it is very suitable for some special industries and grinding materials.
Especially for milling and dispersing high viscosity pastes and high purity products.
●Technical Parameters:
Composition | Wt% | 20% CeO2 + 80% ZrO2 |
Specific Density | g/cm3 | 6.0 |
Color | — | Yellow/Gold |
Bulk Density | g/cm3 | 3.85 |
Hardness | Mohs | 9 |
Elastic Modulus | GPA | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥2000(ø2mm) |
Fracture Toughness | Mpam1-2 | 8.5 |
Thermal Expansion Coefficient |
10*10-6/℃(20-400) | 9.0 |
Wear Loss |
ppm/hr |
<10ppm/hr(24h) |
Grain Size | μm |
≤0.5 |
●Size:
Size (mm) | Size (mm) | Size (mm) | Size (mm) |
0.3-0.5m | 1.0-1.2 | 1.8-2.0 | 2.6-2.8 |
0.4-0.6 | 1.2-1.4 | 2.0-2.2 | 2.8-3.0 |
0.6-0.8 | 1.4-1.6 | 2.2-2.4 | 3.0-3.2 |
0.8-1.0 | 1.6-1.8 | 2.4-2.6 | 5, 8, 10, 20. |
●Application:
(1).Wear-resistant, corrosion-resistant products: paints, textiles, paints, printing and dyeing;
(2). High strength, high toughness products: magnetic materials, piezoelectric ceramics, dielectric ceramics ;
(3).To prevent pollution: medicine, food, cosmetics ;
(4).Ceramics: Electronic ceramics, refractory ceramics, structural ceramics.
●Feature:
It has a gem-like hardness and density.Micro-structure of delicate, uniform, dense ceramics of the Quartet. Its excellent wear resistance and fracture toughness is particularly suited for grinding and dispersing high-solid-phase high-viscosity, high hardness of the paste.
(1).Long working life: 30 times longer life than glass beads, 6 times than zirconium silicate beads.
(2)High grindingefficiency: around 6 times than glass beads; 2 times than zirconium silicate bead
(3).Excellent wear resistance and fracture toughness.
●Package:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
●Storage:
The grinding media should be stored in a dry and clean place.
●Product Introdution:
It is with the earth rare element “cerium”, so cerium stabilized zirconia bead has the biggest specific gravity in all zirconia beads series and it is very suitable for some special industries and grinding materials.
Especially for milling and dispersing high viscosity pastes and high purity products.
●Technical Parameters:
Composition | Wt% | 20% CeO2 + 80% ZrO2 |
Specific Density | g/cm3 | 6.0 |
Color | — | Yellow/Gold |
Bulk Density | g/cm3 | 3.85 |
Hardness | Mohs | 9 |
Elastic Modulus | GPA | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥2000(ø2mm) |
Fracture Toughness | Mpam1-2 | 8.5 |
Thermal Expansion Coefficient |
10*10-6/℃(20-400) | 9.0 |
Wear Loss |
ppm/hr |
<10ppm/hr(24h) |
Grain Size | μm |
≤0.5 |
●Size:
Size (mm) | Size (mm) | Size (mm) | Size (mm) |
0.3-0.5m | 1.0-1.2 | 1.8-2.0 | 2.6-2.8 |
0.4-0.6 | 1.2-1.4 | 2.0-2.2 | 2.8-3.0 |
0.6-0.8 | 1.4-1.6 | 2.2-2.4 | 3.0-3.2 |
0.8-1.0 | 1.6-1.8 | 2.4-2.6 | 5, 8, 10, 20. |
●Application:
(1).Wear-resistant, corrosion-resistant products: paints, textiles, paints, printing and dyeing;
(2). High strength, high toughness products: magnetic materials, piezoelectric ceramics, dielectric ceramics ;
(3).To prevent pollution: medicine, food, cosmetics ;
(4).Ceramics: Electronic ceramics, refractory ceramics, structural ceramics.
●Feature:
It has a gem-like hardness and density.Micro-structure of delicate, uniform, dense ceramics of the Quartet. Its excellent wear resistance and fracture toughness is particularly suited for grinding and dispersing high-solid-phase high-viscosity, high hardness of the paste.
(1).Long working life: 30 times longer life than glass beads, 6 times than zirconium silicate beads.
(2)High grindingefficiency: around 6 times than glass beads; 2 times than zirconium silicate bead
(3).Excellent wear resistance and fracture toughness.
●Package:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
●Storage:
The grinding media should be stored in a dry and clean place.
●Chemical Composition:
Composition | ZrO₂ | CeO₂ + Others |
Content % | ≥80 | ≤20 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Bending Strength MPa | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load Kgf(Φ1.50mm) | Sphericity (%) |
≥5.95 | ≥3.70 | 1000-1200 | ≥1150 | 7 | ≥70 | ≥98 |
●Sizes Φ:
Size (mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.6-2.8 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 2.8-3.0 |
Note: Size can be customized as per request.
●Chemical Composition:
Composition | ZrO₂ | CeO₂ + Others |
Content % | ≥80 | ≤20 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Bending Strength MPa | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load Kgf(Φ1.50mm) | Sphericity (%) |
≥5.95 | ≥3.70 | 1000-1200 | ≥1150 | 7 | ≥70 | ≥98 |
●Sizes Φ:
Size (mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.6-2.8 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 2.8-3.0 |
Note: Size can be customized as per request.