Zirconia ball has a pearl luster and smooth working sphere, dense internal structure, super high densiry , strong compressive strength and super high wear resistance, and is a high-end product in abrasive media. However, this product has a high requirement for the use of the hardness of the memory material in the grinding machine.
1. Main Advantage of the zirconia bead/ball
· Excellent wear resistance, Weight loss of ball lee of 4ppm,
· High density, grinding efficiency,
· No impurity, keep the material high degree of purity.
2. Main Use of the zirconia bead/ball
· Electronic material (Such as BaTiO3,BaCO3), Magnetic bands superfine grinding,
· Paint,pigment, Coatings dispesing and superfine grinding,
· Ceramic glaze(zirconia sand) superfine grinding,
· Medication, Cosmetic dispersing and superfine grinding.
3. Available Size
Sphere: Φ0.1-0.3mm, Φ0.6, Φ0.8, Φ1, Φ1.5,Φ2, Φ2.5,Φ3,Φ5, Φ6.5Φ7,Φ10,Φ12,Φ15,Φ20, Φ30,Φ55,Φ60mm
Cylinder: Φ3*3, Φ5*5, Φ7*7, Φ10*10, Φ12*12mm
4. Material Properties
Composition | wt% | 94.6%ZrO2,5.4Y2O3 |
Specific density | g/cm3 | ≥6.02g/cm3 |
Hardness(HV) | HRA | >10 |
Thermal expansion | X10-6/K | 11 |
Coefficient(20400) | ||
Elastic modulis | GPa | 205 |
Fracture toughness | Mpa·m1/2 | 7-10 |
Bending strength | MPa | 1150 |
Grain size | Um | <0.5 |
Thermal conductivity | w/(m·k) | 3 |
● Applications:
It is widely used for grinding, dispersing and polishing as following: inkjets inks, electronic slurries, raw material of battery, screen printing inks, coating, painting, pigment, ceramic and cosmetic and other nano particles products.
● Package:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
● Storage:
The grinding media should be stored in a dry and clean place.
●FAQ
A: Please send your drawing or the details of your demand to us, then we will quote to you.
A: Generally it will take about 25-30 days because the production process is a long time cycle, but if we have stock of the products you need, then we can ship out once we get the payment.
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
A: We required 100% TT payment in advance because the products are customized.
Zirconia ball has a pearl luster and smooth working sphere, dense internal structure, super high densiry , strong compressive strength and super high wear resistance, and is a high-end product in abrasive media. However, this product has a high requirement for the use of the hardness of the memory material in the grinding machine.
1. Main Advantage of the zirconia bead/ball
· Excellent wear resistance, Weight loss of ball lee of 4ppm,
· High density, grinding efficiency,
· No impurity, keep the material high degree of purity.
2. Main Use of the zirconia bead/ball
· Electronic material (Such as BaTiO3,BaCO3), Magnetic bands superfine grinding,
· Paint,pigment, Coatings dispesing and superfine grinding,
· Ceramic glaze(zirconia sand) superfine grinding,
· Medication, Cosmetic dispersing and superfine grinding.
3. Available Size
Sphere: Φ0.1-0.3mm, Φ0.6, Φ0.8, Φ1, Φ1.5,Φ2, Φ2.5,Φ3,Φ5, Φ6.5Φ7,Φ10,Φ12,Φ15,Φ20, Φ30,Φ55,Φ60mm
Cylinder: Φ3*3, Φ5*5, Φ7*7, Φ10*10, Φ12*12mm
4. Material Properties
Composition | wt% | 94.6%ZrO2,5.4Y2O3 |
Specific density | g/cm3 | ≥6.02g/cm3 |
Hardness(HV) | HRA | >10 |
Thermal expansion | X10-6/K | 11 |
Coefficient(20400) | ||
Elastic modulis | GPa | 205 |
Fracture toughness | Mpa·m1/2 | 7-10 |
Bending strength | MPa | 1150 |
Grain size | Um | <0.5 |
Thermal conductivity | w/(m·k) | 3 |
● Applications:
It is widely used for grinding, dispersing and polishing as following: inkjets inks, electronic slurries, raw material of battery, screen printing inks, coating, painting, pigment, ceramic and cosmetic and other nano particles products.
● Package:
25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped.
● Storage:
The grinding media should be stored in a dry and clean place.
●FAQ
A: Please send your drawing or the details of your demand to us, then we will quote to you.
A: Generally it will take about 25-30 days because the production process is a long time cycle, but if we have stock of the products you need, then we can ship out once we get the payment.
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
A: We required 100% TT payment in advance because the products are customized.
●Chemical Composition:
Composition | ZrO₂ | Y₂O₃ | Other |
Content % | 94.8±0.2 | 5.1±0.1 | 0.1% |
●Physical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load KN(Φ2.0mm) | Grain size | Wear loss | Sphericity |
≥6.02 | ≥ 3.70 | ≥1250 | 9 | ≥20 | ≤0.5 | ≤0.08 | ≥98 |
● Ball Sizes :
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ0.08-0.12 | Φ0.12-0.18 | Φ0.18-0.22 | Φ0.22-0.28 | Φ0.28-0.35 |
Φ0.3-0.4 | Φ0.4-0.6 | Φ0.6-0.8 | Φ0.8-1.0 | Φ1.0-1.2 |
Φ1.2-1.4 | Φ1.4-1.6 | Φ1.6-1.8 | Φ1.8-2.0 | 2.0-2.2 |
Φ2.2-2.4 | Φ2.4-2.6 | Φ2.6-2.8 | Φ2.8-3.0 | Φ3.0-3.2 |
Φ3.2-3.5 | Φ4 | Φ5 | Φ6 | Φ7 |
Φ8 | Φ10 | Φ12 | Φ15 | Φ17 |
Φ20 | Φ25 | Φ30 | Φ40 | Φ50 |
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ3*3 | Φ5*5 | Φ7*7 | Φ10*10 | Φ12.7*12.7 | Φ15*15 |
●Chemical Composition:
Composition | ZrO₂ | Y₂O₃ | Other |
Content % | 94.8±0.2 | 5.1±0.1 | 0.1% |
●Physical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Hv | Fracture Toughness MPam1-2 | Crushing Load KN(Φ2.0mm) | Grain size | Wear loss | Sphericity |
≥6.02 | ≥ 3.70 | ≥1250 | 9 | ≥20 | ≤0.5 | ≤0.08 | ≥98 |
● Ball Sizes :
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ0.08-0.12 | Φ0.12-0.18 | Φ0.18-0.22 | Φ0.22-0.28 | Φ0.28-0.35 |
Φ0.3-0.4 | Φ0.4-0.6 | Φ0.6-0.8 | Φ0.8-1.0 | Φ1.0-1.2 |
Φ1.2-1.4 | Φ1.4-1.6 | Φ1.6-1.8 | Φ1.8-2.0 | 2.0-2.2 |
Φ2.2-2.4 | Φ2.4-2.6 | Φ2.6-2.8 | Φ2.8-3.0 | Φ3.0-3.2 |
Φ3.2-3.5 | Φ4 | Φ5 | Φ6 | Φ7 |
Φ8 | Φ10 | Φ12 | Φ15 | Φ17 |
Φ20 | Φ25 | Φ30 | Φ40 | Φ50 |
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
Φ3*3 | Φ5*5 | Φ7*7 | Φ10*10 | Φ12.7*12.7 | Φ15*15 |