● Product Introduction:
Zirconium silicate ceramic balls and beads as ceramic grinding media are made from imported Australian zircon sand by using rolling into billets and sintering phase technology, sophisticated technologies provide our customers zirconium silicate grindidng medias of both high compressive strength and low abrasiveness. Compared with alumina and glass balls, zirconium silicate grinding media balls have the advantages of low abrasiveness and high toughness.
● Product Description:
Item | Unit | Specification |
Composition | wt% | 60-65% ZrO2 |
Bulk Density | Kg/L | >2.6-2.7(Φ2mm) |
Specific Density | g/cm3 | ≥4.0 |
Hardness | Moh's | >8.5
|
Elastic modulus | GPa | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥15 (Φ2mm) |
Fracture Toughness | MPam1-2 | 8 |
Grain size | µm | ≤0.5 |
Wear loss | ppm/h | <0.8 |
Size(mm) | ||
0.4-0.6mm | 0.6-0.8mm | 0.8-1.0mm |
1.4-1.4mm | 1.4-1.6mm | 1.6-1.8mm |
2.4-2.6mm | 2.6-2.8mm | 2.8-3.0mm |
● Features:
Compacted and homogeneous microstructure.
High gravity, lower bead wear loss.
High crushing strength, minimum friction to allow minimum wear down to the equipment.
Smooth surface, deeply polished surface, easy wash.
● Applications:
● Factory Process & Qc Equipment:
● Package & Delivery:
20~25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped
● Storage:
The grinding media should be stored in a dry and clean place.
● Product Introduction:
Zirconium silicate ceramic balls and beads as ceramic grinding media are made from imported Australian zircon sand by using rolling into billets and sintering phase technology, sophisticated technologies provide our customers zirconium silicate grindidng medias of both high compressive strength and low abrasiveness. Compared with alumina and glass balls, zirconium silicate grinding media balls have the advantages of low abrasiveness and high toughness.
● Product Description:
Item | Unit | Specification |
Composition | wt% | 60-65% ZrO2 |
Bulk Density | Kg/L | >2.6-2.7(Φ2mm) |
Specific Density | g/cm3 | ≥4.0 |
Hardness | Moh's | >8.5
|
Elastic modulus | GPa | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥15 (Φ2mm) |
Fracture Toughness | MPam1-2 | 8 |
Grain size | µm | ≤0.5 |
Wear loss | ppm/h | <0.8 |
Size(mm) | ||
0.4-0.6mm | 0.6-0.8mm | 0.8-1.0mm |
1.4-1.4mm | 1.4-1.6mm | 1.6-1.8mm |
2.4-2.6mm | 2.6-2.8mm | 2.8-3.0mm |
● Features:
Compacted and homogeneous microstructure.
High gravity, lower bead wear loss.
High crushing strength, minimum friction to allow minimum wear down to the equipment.
Smooth surface, deeply polished surface, easy wash.
● Applications:
● Factory Process & Qc Equipment:
● Package & Delivery:
20~25KG/Plastic Drum, 800-1000KG/Pallet with shrink wrapped
● Storage:
The grinding media should be stored in a dry and clean place.
●Chemical Composition:
Composition | ZrO₂ | SiO₂ |
Content % | 65 | 35 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Moh’s | Hardness Hv | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | light yellow |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 | 4 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 | 5 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 | 6 |
●Chemical Composition:
Composition | ZrO₂ | SiO₂ |
Content % | 65 | 35 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Hardness Moh’s | Hardness Hv | Color |
≥4.0 | >2.5 | ≥7.0 | >900 | light yellow |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | Size(mm) |
0.4-0.6 | 1.0-1.2 | 1.6-1.8 | 2.4-2.6 | 4 |
0.6-0.8 | 1.2-1.4 | 1.8-2.0 | 2.5-3.0 | 5 |
0.8-1.0 | 1.4-1.6 | 2.2-2.4 | 3.0-3.5 | 6 |