●Product Introduction:
Kingda ceria zirconia grinding beads has a gem-like hardness and density, It is the heaviest of all zirconium series grinding media, larger impact energy can be obtained in the grinding equipment, thereby enhancing production efficiency. It has excellent abrasion resistance and fracture toughness, especially for high viscosity or abrasive products with high solid and easier to show its advantages. The low viscosity of the product, as a result of the option at a fixed volume of the smaller, cerium stabilized zirconia abrasive grinding surface area increased referrals, and then grinding to obtain better results.
●Technical Data Sheet:
Item | Unit | Specification |
Composition | wt% | 78-80% ZrO2 |
Bulk Density | Kg/L | >3.6(Φ2mm) |
Specific Density | g/cm3 | ≥6.0 |
Hardness | Moh's | >8.5 |
Elastic modulus | GPa | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥20 (Φ2mm) |
Fracture Toughness | MPam1-2 | 9 |
Grain size | µm | ≤0.5 |
Wear loss | ppm/h | <0.15 |
Regular Size
0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.5-0.6mm 0.6-0.8mm 0.8-1.0mm 1.0-1.2mm
1.4-1.6mm 1.6-1.8mm 1.8-2.0mm 2.0-2.2mm 2.2-2.4mm 2.4-2.8mm 2.8-3.2mm
●Application:
(1) Ultrafine dispersion and grinding in paint, ink, coatings, papermaking, pigment, dye and other industries.
(2) Superfine grinding of electronic material, magnetic material and nanometer material.
(3) Ultrafine grinding and dispersion of chemical fiber, titanium dioxide and glaze.
(4) Ultrafine grinding and dispersion of medication, food and cosmetics.
●Advantages:
(1) Wide application range, especially for grinding materials with high hardness and viscosity.
(2) Larger density
(3) Resistance to a variety of chemical liquids corrosion.
(4) Smooth surface, easy to clean
(5) High impact resistance, no break under high speed operation.
(6) High grinding efficiency, low wear loss and low comprehensive cost.
●Packing & Delivery:
●Product Introduction:
Kingda ceria zirconia grinding beads has a gem-like hardness and density, It is the heaviest of all zirconium series grinding media, larger impact energy can be obtained in the grinding equipment, thereby enhancing production efficiency. It has excellent abrasion resistance and fracture toughness, especially for high viscosity or abrasive products with high solid and easier to show its advantages. The low viscosity of the product, as a result of the option at a fixed volume of the smaller, cerium stabilized zirconia abrasive grinding surface area increased referrals, and then grinding to obtain better results.
●Technical Data Sheet:
Item | Unit | Specification |
Composition | wt% | 78-80% ZrO2 |
Bulk Density | Kg/L | >3.6(Φ2mm) |
Specific Density | g/cm3 | ≥6.0 |
Hardness | Moh's | >8.5 |
Elastic modulus | GPa | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥20 (Φ2mm) |
Fracture Toughness | MPam1-2 | 9 |
Grain size | µm | ≤0.5 |
Wear loss | ppm/h | <0.15 |
Regular Size
0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.5-0.6mm 0.6-0.8mm 0.8-1.0mm 1.0-1.2mm
1.4-1.6mm 1.6-1.8mm 1.8-2.0mm 2.0-2.2mm 2.2-2.4mm 2.4-2.8mm 2.8-3.2mm
●Application:
(1) Ultrafine dispersion and grinding in paint, ink, coatings, papermaking, pigment, dye and other industries.
(2) Superfine grinding of electronic material, magnetic material and nanometer material.
(3) Ultrafine grinding and dispersion of chemical fiber, titanium dioxide and glaze.
(4) Ultrafine grinding and dispersion of medication, food and cosmetics.
●Advantages:
(1) Wide application range, especially for grinding materials with high hardness and viscosity.
(2) Larger density
(3) Resistance to a variety of chemical liquids corrosion.
(4) Smooth surface, easy to clean
(5) High impact resistance, no break under high speed operation.
(6) High grinding efficiency, low wear loss and low comprehensive cost.
●Packing & Delivery:
●Chemical Composition:
Composition | ZrO₂ | CeO₂ | Others |
Content % | 85~88 | 10~14 | <3 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Compressive Strength (Φ2.0mm) | Hardness Hv | Self-Consumption (ppm/h) | Color | Sphericity (%) |
≥6.15 | ≥3.75 | >2.0KN | ≥1180 | <0.7 | Black grey | ≥99 |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | |
0.4-0.5 | 0.6-0.8 | 0.9-1.0 | 1.4-1.6 | 2.2-2.5 |
0.4-0.6 | 0.7-0.8 | 0.9-1.1 | 1.6-1.8 | 2.5-2.8 |
0.5-0.7 | 0.7-0.9 | 1.0-1.2 | 1.8-2.0 | 2.8-3.2 |
0.6-0.7 | 0.8-1.0 | 1.2-1.4 | 2.0-2.2 | 3.2-3.5 |
Note: Size can be customized as per request.
●Chemical Composition:
Composition | ZrO₂ | CeO₂ | Others |
Content % | 85~88 | 10~14 | <3 |
●Typical Properties:
Specific Gravity g/cm³ | Bulk Density g/cm³ | Compressive Strength (Φ2.0mm) | Hardness Hv | Self-Consumption (ppm/h) | Color | Sphericity (%) |
≥6.15 | ≥3.75 | >2.0KN | ≥1180 | <0.7 | Black grey | ≥99 |
●Sizes Φ:
Size(mm) | Size(mm) | Size(mm) | Size(mm) | |
0.4-0.5 | 0.6-0.8 | 0.9-1.0 | 1.4-1.6 | 2.2-2.5 |
0.4-0.6 | 0.7-0.8 | 0.9-1.1 | 1.6-1.8 | 2.5-2.8 |
0.5-0.7 | 0.7-0.9 | 1.0-1.2 | 1.8-2.0 | 2.8-3.2 |
0.6-0.7 | 0.8-1.0 | 1.2-1.4 | 2.0-2.2 | 3.2-3.5 |
Note: Size can be customized as per request.